Ike dị elu karịa alumina
Ọnụ ala karịa zirconia
Nguzogide iyi pụrụiche
Nnukwu nguzogide corrosion
Ike mgbaji dị elu
Nkwụsi ike dị elu nke okpomọkụ
A na-eji eriri seramiiki roba na-eguzogide ọgwụ na-enye uwe dị elu yana nchebe mmetụta.
1) Jikọta ike na-amịkọrọ roba na ọmarịcha abrasion na-eguzogide elu alumina seramiiki, dabara maka akwa akwa na ngwa mmetụta.
2) Ụdị na nha nke omenala iji gboo ihe ị chọrọ, ọkọlọtọ liners na ndị na-abụghị ọkọlọtọ dị.
3) Ngwọta iyi na abrasion zuru oke
4) Onye nrụpụta nwere ahụmahụ bara ụba, ezigbo njikọ dị n'etiti roba na seramiiki, ceramics na-anọ ebe ahụ ruo mgbe ọ ga-eyi kpamkpam.
5) Ihe dị iche iche nke efere seramiiki roba iji gboo ihe dị iche iche ị chọrọ.
1) Bunker
2) Nri chute
3) Mgbochi mkpofu
4) Ore nchekwa
5) Ọkpụkpụ
6) Bịnụ
| IKPEHE | ALA | UNIT | ZTA Ceramic |
| Ceramic | Al2O3 | % | 70-75 |
| ZrO2 | % | 25-30 | |
| Njupụta | g/cm3 | 4.20 | |
| Vickers isi ike | kg/mm2 | 1300 | |
| Mgbaji siri ike | Mpa.M1/2 | 3-4 | |
| Rubber | Ike mgbanwe | Mpa | 680 |
| Ihe mejupụtara | - | Nature rubber+SBR | |
| Ike ike mmiri | HA | 60±5 | |
| Ọnụọgụ elongation tensile | % | > 400 | |
| Ike ọdụdọ | Mpa | 25 | |
| Ike akwa mmiri(%) | % | 30 | |
| Ike njide n'etiti roba na seramiiki | Mpa | 4 | |
| Igwe igwe | Ihe onwunwe | - | Q235A |
| Ike njupụta | g/cm3 | 7.85 | |
| Ọkpụrụkpụ | mm | 5-6 | |
| Nrapado | Ọdịdị | - | Mmiri mmiri na-acha aja aja |
| Ọdịnaya siri ike | - | 20± 3% | |
| Viscosity | Mpa | ≥2.5 | |
| Bee ike | 48h N/2.5cm | ≥120 | |
| Ike mkpakọ | Mpa | ≥850 | |
| Ọnọdụ okpomọkụ na-arụ ọrụ | ºC | -20 - 100 |
Anyị na-anabata iwu omenala.
Ọ bụrụ na ịchọrọ ịmatakwu ozi ngwaahịa, biko nweere onwe gị ịkpọtụrụ anyị ma anyị ga-enye gị ngwaahịa kachasị mma na ọrụ kacha mma!